標準號：BS EN ISO 604-2003
中文標準名稱：塑料.壓縮性能的測定
英文標準名稱：Plastics - Determination of compressive properties
標準類型：G31
發布日期：2003/8/7 12:00:00
實施日期：2003/8/7 12:00:00
中國標準分類號：G31
國際標準分類號：83.080.01
適用范圍：This International Standard specifies a method for determining the compressive properties of plastics under defined conditions. A standard test specimen is defined but its length may be adjusted to prevent buckling under load from affecting the results. A range of test speeds is included. The method is used to investigate the compressive behaviour of the test specimens and for determining the compressive strength, compressive modulus and other aspects of the compressive stress/strain relationship under the conditions defined. The method applies to the following range of materials: — rigid and semi-rigid!1] thermoplastic moulding and extrusion materials, including compounds filled and reinforced by e.g. short fibres, small rods, plates or granules in addition to unfilled types; rigid and semi-rigid thermoplastic sheet; — rigid and semi-rigid thermoset moulding materials, including filled and reinforced compounds; rigid and semi-rigid thermoset sheet; — thermotropic liquid-crystal polymers. In agreement with IS010350-1 and IS010350-2, this International Standard applies to fibre-reinforced compounds with fibre lengths ≤7,5 mm prior to processing. The method is not normally suitable for use with materials reinforced by textile fibres (see references [2] and [5]), fibre-reinforced plastic composites and laminates (see [5]), rigid cellular materials (see [3]) or sandwich structures containing cellular material or rubber (see [4]). The method is performed using specimens which may be moulded to the chosen dimensions, machined from the central portion of a standard multipurpose test specimen (see ISO 3167) or machined from finished or semi-finished products such as mouldings or extruded or cast sheet. The method specifies preferred dimensions for the test specimen. Tests which are carried out on specimens of different dimensions, or on specimens which are prepared under different conditions, may produce results which are not comparable. Other factors, such as the test speed and the conditioning of the specimens, can also influence the results. Consequently, when comparable data are required, these factors must be carefully controlled and recorded.