標準號：SAE AMS 4613-2011
中文標準名稱：溶解熱處理,冷加工(8%)和沉淀熱處理工藝制備的6.3Cu-0.30Mn-0.06Ti-0.10V-0.18Zr鋁合金薄板和厚板(2219-T87)
英文標準名稱：Aluminum Alloy, Sheet and Plate 6.3Cu 0.30Mn 0.06Ti 0.10V 0.18Zr Solution Heat Treated, Cold Worked (8%) and Precipitation Heat Treated (2219-T87)
標準類型：V11
發布日期：2011/7/8 12:00:00
實施日期：1999/12/31 12:00:00
中國標準分類號：V11
國際標準分類號：49.025.20
引用標準：ANSI H 35.2-2009;ANSI H 35.2M-2009;ASTM B 594-2009;ASTM B 666-1990;ASTM B 666M-1990;ASTM E 8-2004;ASTM E 8M-2004;ASTM E 1409-2008;ASTM E 1447-2009;ASTM E 1941-2010;ASTM E 2371-2004;SAE AMS 2355;SAE AMS 2772-1997;SAE ARP 823;SAE AS 1990-1990
適用范圍：This specification covers an aluminum alloy in the form of sheet and plate. These products have been used typically for parts requiring high strength up to 500 φF (260 φC), but usage is not limited to such applications. Material may be welded in the specified condition but properties are improved by reheat treatment after welding. Reheat treatment after welding, however, may reduce resistance to stress-corrosion cracking. Certain design and processing procedures may cause these products to become susceptible to stress-corrosion cracking; ARP823 recommends practices to minimize such conditions.