標(biāo)準(zhǔn)號：SAE AMS 5355J-2009
中文標(biāo)準(zhǔn)名稱：鋼熔模鑄件16Cr 4.1Ni 0.28Cb 3.2Cu均化作用和溶解熱處理或均化作用、溶解和沉淀物熱處理的耐腐蝕性和耐熱性
英文標(biāo)準(zhǔn)名稱：Steel, Corrosion Resistant, Investment Castings 16Cr 4.1Ni 0.28Cb 3.2Cu Homogenization and Solution Heat Treated or Homogenization, Solution, and Precipitation Heat Treated
標(biāo)準(zhǔn)類型：V11
發(fā)布日期：2009/10/23 12:00:00
實施日期：1999/12/31 12:00:00
中國標(biāo)準(zhǔn)分類號：V11
國際標(biāo)準(zhǔn)分類號：49.025.10
引用標(biāo)準(zhǔn)：ASTM E 8/E 8M-2008;ASTM E 8/E 8M-2009;ASTM E 18-2008;ASTM E 353-1993;ASTM E 1417-2005;ASTM E 1444-2005;ASTM E 1742-2008;SAE AMS-H-6875-1998;SAE AMS 2175-2003;SAE AMS 2248F-2006;SAE AMS 2360D-2007;SAE AMS 2694B-2007;SAE AMS 2700-2000;SAE AMS 2804C-2001;SAE
適用范圍：This specification covers a corrosion-resistant steel in the form of investment castings. These castings have been used typically for parts requiring good corrosion resistance and strength up to 600 °F (316 °C), but usage is not limited to such applications. Certain processing procedures and service conditions may cause these castings to become subject to stress-corrosion cracking; ARP1110 recommends practices to minimize such conditions. Where stress-corrosion is considered to be a factor, precipitation heat treatment should be performed at a temperature not lower than 1000 °F (538 °C).