標準號：SAE AMS 5617J-2006
中文標準名稱：12Cr、8.5Ni、1.2Ti和2.0Cu真空感應和真空自耗電*熔化溶液熱處理、沉淀硬化的耐腐蝕鋼棒材、線材和鍛件
英文標準名稱：Steel Bars, Wire, and Forgings, Corrosion Resistant 12Cr - 8.5Ni - 1.2Ti - 2.0Cu Vacuum Induction Plus Vacuum Consumable Electrode Melted Solution Heat Treated, Precipitation Hardenable UNS S45500
標準類型：V11
發布日期：2006/5/20 12:00:00
實施日期：1999/12/31 12:00:00
中國標準分類號：V11
國際標準分類號：49.025.10
引用標準：ASTM A 370-2005;ASTM A 370-2006;ASTM A 604-1993;ASTM E 45-2005;ASTM E 112-1996;ASTM E 353-1993;SAE AMS 2241P-2005;SAE AMS 2248F-2006;SAE AMS 2300K-2003;SAE AMS 2371G-2003;SAE AMS 2374D-2002;SAE AMS 2750D-2005;SAE AMS 2806B-2000;SAE AMS 2808D-2001;SAE ARP
適用范圍：This specification covers two grades of a premium aircraft-quality, corrosion-resistant steel in the form of bars, wire, forgings, and forging stock. These products have been used typically for parts requiring corrosion resistance and high strength up to 800 °F (425mDC). The steel can be precipitation hardened to minimum tensile strengths up to 225,000 psi (1550 Mpa). Certain design and processing procedures may causes these products to become susceptible to stress-corrosion cracking after heat treatment; ARP 1110 recommends practices to minimize such conditions.